sgoertz

This was done with my miller syncrowave 180sd
settings were:

.045 308l filler rod
3/32nd 2% thoricated tungsten
17 series torch
#8 gas lens
20 cfh flow, 15cfh purge flow
60 amps

Material is 1.75" 304 stainless 16 gauge, the same stuff I am building my new tubulars out of (top mount, sidewinder)









-James

MikeJ-2009

Get over yourself. This isn't honda-tech.

Schister66

i don't understand the last comment... .if you were asking an honest opinion i would say they're pretty good, but if you were doing that just to brag, then i agree...."Get over yourself!"

MikeJ-2009

<---trend setter.

sgoertz

actually i am still not happy as they are not burnsstainless yet....
if engloid was on here he could give some real advise as to how to get the perfect band of gold they get but i guess all yall think about is how to cut people down so poo on you
-James

MikeJ-2009

Ok OK. James, how did you do it? Did Jesus teach you to weld? How much would it be to autograph my ****?

N1ghtM0nkey

The only thing I know to look for is a stack of dimes.

Meaning the weld should look like a stack of dimes overlapping each other.

In that area you get an A. I've seen better, but that is impressive.

BarelyBoosted

Alot better than me...Good penatration(no jokes), but if I had to give some construtive critisizm* the bead could be a little tighter and a little more consistansy* in the size but that just for looks of course.

Edit: It's late and my spelling sux.

MikeJ-2009

James, you need to go to the "Smiley Hotrex school of Welding"


If you're not plugging into your mothers dryer, you just aren't doing it right.

88dx

Looks like your welding sober, you def need to drink a six pack of PBR before your touch the welder t