I run about 70 - 80A pusled, 75% on time, about 10hz - 50hz , 50% background current, 3/32 Trimix, 25 cfh thiner ---- I drop to 1/16 2% thor and turn my flow meter to 35 cfh so I can cool faster. Run shorter passes other wise you get massive warping and contraction of the work piece. Looks pretty good though. I get to see how good mine are this week its been awhile

#Rotor

you really want me to post 700+ pics..... it's gonna take me a month to write the BB-code for that.....

SkunT

james you make me sick.

sgoertz

here is what those blinging welds were for








My assurance of quality ^^

-James

JonDouglas

That gives me a chubby. Excellent work as always man.

Engloid

Looks good on the outside... but why no bevel or gap? It's hard to get smooth penetration without it.

sgoertz

the only joints that were like that were right there at the collector, because I knew I was going to have to refit them anyways after welding (the pipes move like 1/4" around when you weld them off the manifold)

I not a total newb to this stuff man

-James

Random Hero

Damn you are a consistant welder! I wish i could be 1/2 as consistant as you.. here is my shot at it

(sorry for the low quality pic)

BigWheeze

Those are pretty good just work on your restarts.