Mani Fresh?
Hey guys, Lack of money and motivation led me to try and weld my turbine housing straight to the manifold. Theres some good welds I think but over all I think it will hold after a bit of grinding and touchup. Let me know what you guys think.
http://pg.photos.yahoo.com/ph/dlloyd...yd80/my_photos |
Re: Mani Fresh?
That will
A: Leak like a sieve. B: End up cracking and falling off. Did you stick weld that using a car battery or something? |
Re: Mani Fresh?
no I used my flux core lincoln (mig) Where do I start to make it better?
|
Re: Mani Fresh?
reweld it sunny! :6
|
Re: Mani Fresh?
Brin git to someone that has a higher amp TIG or Mig and have them blast it on.
|
Re: Mani Fresh?
Where do I start . Please just don't trash me. What did I do wrong ? Too fast? too slow? I'm a supposed to be a Banker? Help me out guys
|
Re: Mani Fresh?
I can go slower on wire feed and one more step up on the Amperage. Would that fix it.
|
Re: Mani Fresh?
Ok turn the heat up all the way and slow the wire feed down. Then go slowly and steady. It should be fine.
|
Re: Mani Fresh?
Ya, Your beads seem to be just "Covering Up" the joint. not penetrating into the material. ARC is the best. I did an adaptor plate to a 14b using my ol' 50yr old arc and some 6013 rod. 2 beads down each side. never seen a crack and never will! Mind ya I was using the highest amprage and hold the stick about 3/4" away!
|
Re: Mani Fresh?
Originally Posted by CSaddict
Ok turn the heat up all the way and slow the wire feed down. Then go slowly and steady. It should be fine.
|