:confused:i am starting my hmt build and will be using a 14b on my y8 engine. i have the turbo apart to rebuild and there are the common cracks in the hotside and in the wastegate hole is it goin to be a problem if i have someone weld these and have it machined or should i just look for another hot side i dont know what to do about this....any help would be great..
|
im in the same situation
i would like to know what people did to |
come on guys its not rocket science or spinal surgery you can leave it with the cracks and it will be fine or you can weld them shut but i doubt you will find one with no cracks 14bs are hard to come by with out cracks
|
You can do any of those 2 options, also you can use it as it for some time.
The second option are cheaper and faster than the first, but first option are good too |